Flame retardant thermoplastic resin composition

ABSTRACT

The present invention relates to a flame retardant polycarbonate thermoplastic resin composition that comprises a polycarbonate resin, a rubber modified vinyl-grafted copolymer, a phosphorous mixture of a cyclic phosphazene oligomer compound and a phosphate ester morpholide compound or a phosphoric acid ester as a flame retardant, and, optionally, a fluorinated polyolefin resin, which has good flame retardancy, heat resistance, mechanical strength, impact strength, heat stability, processability, and appearance.

This application is a continuation in part of Ser. No. 10/489,545 which was a National Stage of International Application No. PCT/KR01/01891, filed Nov. 7, 2001, published in English under PCT Article 21(2) and now abandoned. This application is also a continuation in part of Ser. No. 10/488,449 filed Mar. 3, 2004 now U.S. Pat. No. 7,094,818 which was a National Stage of International Application No. PCT/KR01/01890, filed Nov. 7, 2001, published in English under PCT Article 21(2) and now abandoned.

FIELD OF THE INVENTION

The present invention relates to a polycarbonate thermoplastic resin composition with good flame retardancy, heat resistance and mechanical properties. More particularly, the present invention relates to a flame retardant polycarbonate thermoplastic resin composition that comprises a polycarbonate resin, a rubber modified vinyl-grafted copolymer, a phosphorous compound mixture of a cyclic phosphazene oligomer Compound and a phosphate ester morpholide compound or phosphoric acid ester as a flame retardant, and a fluorinated polyolefin resin, which has good flame retardancy, heat resistance, mechanical strength, impact strength, heat stability, processability, and appearance.

BACKGROUND OF THE INVENTION

To improve flame retardancy of thermoplastic resin composition is a major target to the research and development of the resin for a long time. The flame retardancy is measured by the UL-94 test method of Underwriters Laboratory. In this flame retardancy test, if the specimen is flamed out within 10 seconds after flaming and if the total flame out time is within 50 seconds when five specimens are flamed twice, the resin composition can obtain V-0 degree of flame retardancy.

A blend of a polycarbonate resin and a styrene-containing copolymer is a resin composition which has improved processability maintaining the good notched impact strength. The polycarbonate resin composition should further have good flame retardancy as well as high mechanical strength because the resin composition are applied to electric or electronic goods, automobile parts, office supplies, etc.

To provide the polycarbonate resin with good flame retardancy, a halogen-containing flame retardant and/or an antimony-containing compound were used.

However, the disadvantages could be observed that the halogen-containing compound results in the corrosion of the mold itself by the hydrogen halide gases released during the molding process and is fatally harmful due to the toxic gases liberated in case of fire. Especially, since the polybromodiphenyl ether, mainly used for a halogen-containing flame retardant, can produce toxic gases such as dioxin or furan during combustion, flame retardants which are prepared without a halogen-containing compound have become a major concern in this field. Accordingly, It is a trend to prepare a resin composition using a halogen-free phosphorous compound.

Phosphorous compounds are a representative halogen-free flame retardant. The phosphorous compounds include monophosphate such as triphenylphosphate and tricresilphosphate, and oligomeric phosphate such as resorcinol bis(diphenylphosphate), hydroquinone bis(diphenylphosphate) and bisphenol-A bis(diphnylphosphate). However, as the halogen-free flame retardant shows a poorer flame retardancy than the halogen-containing flame retardant, an excess amount of halogen-free flame retardant should be used to obtain the same degree of flame retardancy. If an excess amount of the flame retardant is used, the impact strength and heat resistance of the resin composition can become severely deteriorated.

Japanese Patent Laid-open No. 2000-154277 discloses a thermoplastic resin composition using phosphoric acid amide as a flame retardant, which improves processability of the resin and hydrolysis resistance of the flame retardant. However, particular phosphoric acid amides cause poor hydrolysis resistance of the flame retardant resin composition. Further, in certain phosphorous acid amides, the flame retardancy and impact strength are severely decreased and the flame retardant becomes volatile to cover the surface of the molded article, so called, to occur juicing phenomenon.

Japanese Patent Laid-open No. 6-100,785 discloses a flame retardant resin composition which comprises a thermoplastic resin, a phosphate compound, and a silicon resin or a polyphosphazene to prevent from dripping of the resin during combustion. However, the Japanese patent application does not disclose that the flame retardancy of the resin composition had been improved.

EP 0 728 811 A2 discloses a thermoplastic resin composition comprising an aromatic polycarbonate, a graft copolymer, a copolymer and a phosphazene. The European patent teaches that no dripping occurs during combustion by using a phosphazene as a flame retardant even though an additional anti-dripping agent is not employed, and that the resin composition has excellent heat resistance and impact strength. However, the resin composition of the European patent has a poor processability due to the poor flowability by using the phosphazene, and causes black stripes and/or black lines on the surface of the molded article due to degradation of the resin or flame retardants when an excess stress is applied to the article during molding. In the European patent using phosphazene as a flame retardant, mechanical strength such as flexural strength and flexural modulus becomes deteriorated, and more flame retardants should be used to maintain a certain degree of flame retardancy.

WO 00/09518 and WO 99/19383 disclose methods of preparing a cross-linked linear or cyclic phenoxy phosphazene and a thermoplastic resin composition using such phosphazene compounds. According to the patent applications, the cross-linked phenoxy phosphazene does not deteriorate the mechanical properties of the resin composition when applied, because the phosphazene has a high melting point and lower volatility. However, the resin composition of the patent applications has a poor processability due to the poor flowability by using the phosphazene, and causes black stripes and/or black lines on the surface of the molded article due to degradation of the resin or flame retardants when an excess stress is applied to the article during molding. In the patent applications using phosphazene as a flame retardant, mechanical strength such as flexural strength and flexural modulus becomes deteriorated.

Any section of the Background of the Invention in parent U.S. Pat. No. 7,094,818 is herein incorporated by reference.

The present inventors have developed a flame retardant thermoplastic resin compositions which have good balance of physical properties such as impact strength, heat resistance, heat stability, processability and appearance. The invention includes compositions which comprise a polycarbonate resin, a rubber modified vinyl-grafted copolymer, a vinyl copolymer, a phosphorous compound mixture of a cyclic phosphazene oligomer compound and a phosphate ester morpholide compound as a flame retardant and a fluorinated polyolefin resin. The invention also includes compositions which comprise a polycarbonate resin, a rubber modified vinyl-grafted copolymer, a vinyl copolymer, an oligomer type cyclic phosphazene compound and a phosphoric acid ester as a flame retardant and a fluorinated polyolefin resin,

Other embodiments of the invention include compositions that do not contain the fluorinated polyolefin resin in situations where the properties provided by the resin are not required or can be provided by other materials or methods.

The filing of this application and the content thereof is not and is not to be construed as any agreement or concession to any rejection or objection made in the parent applications. This application is being filed to preserve Applicants' rights in the inventions, including but not limited to, inventions disclosed in the parent U.S. applications, the international applications, and the foreign priority applications in view of inconsistency in the application of the rules/law relating to patents in the U.S.

SUMMARY OF THE INVENTION

A flame retardant thermoplastic resin composition according to the present invention comprises:

-   -   (A) about 45 to 95 parts by weight of a polycarbonate resin;     -   (B) about 1 to 50 parts by weight of a rubber modified         vinyl-grafted copolymer prepared by graft-polymerizing (b₁)         about 5 to 95 parts by weight of a monomer mixture of about 50         to 95% by weight of styrene, α-methylstyrene, halogen- or         alkyl-substituted styrene, C₁₋₈ methacrylic acid alkyl ester,         C₁₋₈ acrylic acid alkyl ester, or a mixture thereof and about 5         to 50% by weight of acrylonitrile, methacrylonitrile, C₁₋₈         methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester,         maleic acid anhydride, C₁₋₄ alkyl- or phenyl N-substituted         maleimide or a mixture thereof onto (b₂) about 5 to 95 parts by         weight of a rubber polymer selected from the group consisting of         butadiene rubber, acryl rubber, ethylene-propylene rubber,         styrene-butadiene rubber, acrylonitrile-butadiene rubber,         isoprene rubber, copolymer of ethylene-propylene-diene (EPDM),         polyorganosiloxane-polyalkyl (meth)acrylate rubber or a mixture         thereof;     -   (C) about 0 to 50 parts by weight of a vinyl copolymer         polymerized with (c₁) about 50 to 95% by weight of styrene,         α-methylstyrene, halogen- or alkyl-substituted styrene, C₁₋₈         methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, or         a mixture thereof and (c₂) about 5 to 50% by weight of         acrylonitrile, methacrylonitrile, C₁₋₈ methacrylic acid alkyl         ester, C₁₋₈ acrylic acid alkyl ester, maleic acid anhydride,         C₁₋₄ alkyl- or phenyl N-substituted maleimide or a mixture         thereof;     -   (D) about 1 to 30 parts by weight of a phosphorous mixture as a         flame retardant, per 100 parts by weight of (A)+(B)+(C), of (d₁)         about 1 to 50% by weight of a cyclic phosphazene oligomer         compound or their mixture represented by the following Formula         (I);

-   -   -   where R₁ is alkyl, aryl, alkyl substituted aryl, aralkyl,             alkoxy, aryloxy, amino or hydroxyl, k and m are an integer             from 1 to 10, R₂ is dioxyarylene group of C₆₋₃₀ or a             derivative thereof, and n is 0 or an integer representing             the number of repeating unit and the average value of n in             the phosphazene mixture is 0.3 to 3; and         -   about 99 to 50% by weight of (d₂) or (D₂) wherein (d₂) is a             phosphate ester morpholide compound represented by the             following Formula (II);

-   -   -   where R₃ is a C₆₋₂₀ aryl group or an alkyl-substituted C₆₋₂₀             aryl group, R₄ is a C₆₋₃₀ arylene group or an             alkyl-substituted C₆₋₃₀ arylene group, t is 1 or 2, and x             and y are 0 or integers representing the number of             corresponding units and the average value of (x+y) in the             mixture of phosphate ester morpholide compounds is 0 to 5;             and (D₂) is a phosphoric acid ester; and,

    -   (E) about 0.05 to 5.0 parts by weight of a fluorinated         polyolefin resin with average particle size of about 0.05 to         1000 μm and density of about 1.2 to 2.3 g/Cm³, per 100 parts by         weight of (A)+(B)+(C).

DETAILED DESCRIPTION OF THE INVENTION

A flame retardant thermoplastic resin composition according to the present invention comprises (A) about 45 to 95 parts by weight of a polycarbonate resin, (B) about 1 to 50 parts by weight of a rubber modified vinyl-grafted copolymer, (C) about 0 to 50 parts by weight of a vinyl copolymer, (D) about 1 to 30 parts by weight of a phosphorous mixture of a cyclic phosphazene oligomer and a phosphate ester morpholide, or phosphoric acid ester as a flame retardant, per 100 parts by weight of (A)+(B)+(C), and, optionally, (E) about 0.05 to 5.0 parts by weight of a fluorinated polyolefin resin per 100 parts by weight of (A)+(B)+(C)

(A) Polycarbonate Resin

The polycarbonate resin is prepared by reacting a diphenol represented by the following formula (I) with a phosgene, a halogen formate or a carboxylic acid diester:

where A is a single bond, a C₁₋₅ alkylene group, a C₁₋₅ alkylidene group, a C₅₋₆ cycloalkylidene group, S or SO₂.

The examples of the diphenol include hydroquinone, resorcinol, 4,4′-dihydroxydiphenol, 2,2-bis-(4-hydroxyphenyl)-propane, 2,4-bis-(4-hydroxyphenyl)-2-methylbutane, 1,1-bis-(4-hydroxyphenyl)-cyclohexane, 2,2-bis-(3-chloro-4-hydroxyphenyl)-propane, and 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane. More preferable diphenols are 2,2-bis-(4-hydroxyphenyl)-propane, 2,2-bis-(3,5-dichloro-4-hydroxyphenyl)-propane, and 1,1-bis-(4-hydroxyphenyl)-cyclohexane, and the most preferable diphenol is 2,2-bis-(4-hydroxyphenyl)-propane called ‘bisphenol A’.

In the present invention it is preferable that the polycarbonate resin (A) has a weight average molecular weight (M_(w)) of about 10,000 to 200,000, more preferably about 15,000 to 80,000.

A polycarbonate with branched chains may also be preferably used. In particular a compound with 3 valences or above may be added in an amount of about 0.05 to 2 mol % per the total moles of the diphenol to be used. A homopolymer of polycarbonate, a copolymer of polycarbonate or a mixture thereof may be used in this invention. Some portion of the polycarbonate resin may be replaced with an aromatic polyester-carbonate resin that is obtained by polymerization in the presence of an ester precursor, such as difunctional carboxylic acid. The polycarbonate resin is used in an amount of about 45 to 95 parts by weight as per 100 parts by weight of the flame retardant thermoplastic resin composition according to the present invention. The section relating to the polycarbonate resin in parent U.S. Pat. No. 7,094,818 is herein incorporated by reference.

(B) Rubber Modified Vinyl-Grafted Copolymer

The rubber modified vinyl-grafted copolymer according to the present invention is known in the art. The rubber modified vinyl-grafted copolymer include, but are not limited to, those prepared by graft-polymerizing (b₁) about 5 to 95 parts by weight of a monomer mixture of about 50 to 95% by weight of styrene, α-methylstyrene, halogen- or alkyl-substituted styrene, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, or a mixture thereof and about 5 to 50% by weight of acrylonitrile, methacrylonitrile, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, maleic acid anhydride, C₁₋₄ alkyl- or phenyl N-substituted maleimide or a mixture thereof onto (b₂) about 5 to 95 parts by weight of a rubber polymer selected from the group consisting of butadiene rubber, acryl rubber, ethylene-propylene rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, isoprene rubber, copolymer of ethylene-propylene-diene (EPDM), polyorganosiloxane-polyalkyl(meth)acrylate rubber or a mixture thereof.

The C₁₋₈ methacrylic acid alkyl ester is obtained from methacrylic acid and monohydric alcohol with 1 to 8 carbon atoms and the C₁₋₈ acrylic acid alkyl ester from acrylic acid and monohydric alcohol with 1 to 8 carbon atoms. The examples of the acid alkyl ester include methacrylic acid methyl ester, methacrylic acid ethyl ester, acrylic acid methyl ester, acrylic acid ethyl ester, and methacrylic acid propyl ester. Methacrylic acid methyl ester is the most preferable. Other monomers suitable for inclusion in the monomer mixture can be readily determined by one skilled in the art.

Preferable examples of the rubber modified vinyl-grafted copolymer are grafted-polymers obtained by graft polymerizing a mixture of styrene and acrylonitrile, and, optionally, (meth)acrylic acid alkyl ester onto butadiene rubber, acryl rubber or styrene-butadiene rubber, or by graft polymerizing (meth)acrylic acid alkyl ester onto butadiene rubber, acryl rubber or styrene-butadiene rubber. The most preferable examples of the rubber modified vinyl-grafted copolymer are a grafted-polymer that a mixture of styrene and acrylonitrile is grafted onto butadiene rubber, which is called acrylonitrile-butadiene-styrene (ABS) resin, and a grafted-polymer of MBS resin.

The rubber polymer to prepare the rubber modified vinyl-grafted copolymer has preferably an average particle size of about 0.05 to 4.0 μm considering the impact strength and appearance.

The rubber modified graft copolymer according to the present invention can be prepared through a conventional polymerization process such as emulsion, suspension, solution or bulk process. However, the copolymer can be preferably prepared through the emulsion or bulk process in which vinyl monomers are added to the rubber polymer using an initiator.

The rubber modified vinyl-grafted copolymer is used in an amount of about 1 to 50 parts by weight as per 100 parts by weight of the flame retardant thermoplastic resin composition according to the present invention.

(C) Vinyl Copolymer

The vinyl copolymer of the present invention is a copolymer that is polymerized with (c₁) about 50 to 95% by weight of styrene, α-methylstyrene, halogen- or alkyl-substituted styrene, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, or a mixture thereof and (c₂) about 5 to 50% by weight of acrylonitrile, methacrylonitrile, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, maleic acid anhydride, C₁₋₄ alkyl- or phenyl N-substituted maleimide or a mixture thereof. A mixture of the copolymers may be used as the component (C).

The C₁₋₈ methacrylic acid alkyl ester is obtained from methacrylic acid and monohydric alcohol with 1 to 8 carbon atoms and the C₁₋₈ acrylic acid alkyl ester from acrylic acid and monohydric alcohol with 1 to 8 carbon atoms. The examples of the acid alkyl ester include methacrylic acid methyl ester, methacrylic acid ethyl ester, acrylic acid methyl ester, acrylic acid ethyl ester, and methacrylic acid propyl ester. Methacrylic acid methyl ester is the most preferable.

The vinyl copolymer can be produced as by-products when preparing the rubber modified vinyl-grafted copolymer (B). The by-products are mostly produced when an excess of monomers are grafted onto a small amount of rubber polymer or when a chain transfer agent is used in excess. The amount of the vinyl copolymer to be used in this invention does not include the amount of the by-products that might be produced during preparation of the rubber modified vinyl-grafted copolymer (B).

The preferable examples of the vinyl copolymer are a copolymer of styrene and acrylonitrile, a copolymer of α-methylstyrene and acrylonitrile, and a copolymer of styrene, α-methylstyrene and acrylonitrile. The vinyl copolymer is preferably prepared by emulsion, suspension, solution or bulk process, and has a weight average molecular weight (M_(w)) of about 15,000 to 200,000.

Another preferable examples of the vinyl copolymer (C) are a copolymer prepared from a mixture of methacrylic acid methyl ester monomers and optionally acrylic acid methyl ester monomers. The vinyl copolymer is preferably prepared by emulsion, suspension, solution or bulk process, and has a weight average molecular weight (M_(w)) of about 20,000 to 250,000.

A further preferable example of the vinyl copolymer is a copolymer of styrene and maleic acid anhydride, which is prepared by a continuous bulk process or a solution process. The maleic acid anhydride is preferably used in the amount of about 5 to 50% by weight. The copolymer of styrene and maleic acid anhydride has a weight average molecular weight (M_(w)) of about 20,000 to 200,000 and an intrinsic viscosity of about 0.3 to 0.9.

The styrene for preparation of the component (C) in this invention can be replaced with p-methylstyrene, vinyltoluene, 2,4-dimethylstyrene or α-methylstyrene.

The vinyl copolymer is used in an amount of about 0 to 50 parts by weight as per 100 parts by weight of the flame retardant thermoplastic resin composition according to the present invention. The section relating to the vinyl copolymer (C) in parent U.S. Pat. No. 7,094,818 is herein incorporated by reference.

(D) Phosphorous Compound Mixture of Cyclic Phosphazene Oligomer and Phosphate Ester Morpholide or Phosphoric Acid Ester

The mixture of phosphorous compound is a mixture of (d₁) about 1 to 50% by weight of a cyclic phosphazene oligomer and (d₂) about 99 to 50% by weight of a phosphate ester morpholide. In another embodiment of the invention, the mixture of phosphorous compound is a mixture of (d₁) about 1 to 50% by weight of a cyclic phosphazene oligomer and (D₂) about 99 to 50% by weight of a phosphoric acid ester

(d₁) Cyclic Phosphazene Oligomer

The cyclic phosphazene oligomer is an oligomer type compound or their mixture of the cyclic phosphazene linked with a linking group having a R₂ group, which is represented as following Formula (I):

where R₁ is alkyl, aryl, alkyl substituted aryl, aralkyl, alkoxy, aryloxy, amino or hydroxyl, k and m are an integer from 1 to 10, R₂ is dioxyarylene group of C₆₋₃₀ or a derivative thereof, and n is 0 or an integer representing the number of repeating unit and the average value of n in the mixture of phosphazene compound is 0.3 to 3. The alkoxy and aryloxy groups may be substituted with alkyl, aryl, amino, hydroxyl etc.

In Formula (I), when cyclic phosphazenes of n+1 monomers are linked, the oligomer of cyclic phosphazene is obtained, which has a number average degree of polymerization of n.

It is preferable that the mixture of cyclic phosphazene oligomer has a number average degree of polymerization (n) of 0.3 to 3. In the present invention, cyclic phosphazene oligomers having n value of 0 to 10 may be preferably used in single or in combination as a mixture. The cyclic phosphazene oligomers may be mixed before or after polymerization. The cyclic phosphazene oligomers may have a branched chain.

In Formula (I), the more preferable groups of R₁ are alkoxy, phenoxy and aryloxy, and the most preferable groups of R₁ is phenoxy.

The preferable groups of R₂ are a derivative from catechol, resorcinol, hydroquinone, or the bisphenylenediol of the following formula:

where Y is alkylene of C₁₋₅, alkylidene of C₁₋₅, cycloalkylidene of C₅₋₆, S or SO₂, and z is 0 or 1.

The cyclic phosphazene oligomer of the present invention can be prepared through a conventional method which is not limited. The following method for preparation can be appropriately adopted.

Alkyl alcohol or aryl alcohol reacts with alkali metal hydroxide such as sodium hydroxide and lithium hydroxide to prepare alkali metal alkylate or alkali metal arylate. In the same manner, diol with R₂ group reacts with alkali metal hydroxide to prepare alkali metal diarylate. Cyclic dichlorophophazene reacts with a mixture of the alkali metal alkylate or alkali metal arylate and the alkali metal diarylate, and the resulting solution reacts further with the alkali metal alkylate or alkali metal arylate to obtain the cyclic phosphazene oligomer according to the present invention.

(d₂) Phosphate Ester Morpholide

The phosphate ester morpholide is represented by the following Formula (II). The phosphate ester morpholide may be used in single or in combination as a mixture.

where R₃ is a C₆₋₂₀ aryl group or an alkyl-substituted C₆₋₂₀ aryl group, R₄ is a C₆₋₃₀ arylene group or an alkyl-substituted C₆₋₃₀ arylene group, l is 1 or 2, and x and y are 0 or integers representing the number of corresponding units and the average value of (x+y) in the mixture of phosphate ester morpholide compounds is 0 to 5.

In Formula (II), preferably R₃ is a phenyl group or an alkyl-substituted phenyl group where the alkyl is methyl, ethyl, isopropyl, t-butyl, isobutyl, isoamyl or t-amyl, preferably methyl, ethyl, isopropyl or t-butyl, and R₄ means preferably a C₆₋₃₀ arylene group or an alkyl-substituted C₆₋₃₀ arylene group which is a derivative from resorcinol, hydroquinone or bisphenol-A.

The methods of preparation of the oligomeric phosphate ester morpholide compound are not limited, but the compound is generally prepared by reacting phosphorus oxychloride (POCl₃) with aromatic alcohol with a R₃ group and morpholine at 50-200° C. in the presence of a catalyst by a conventional process to obtain arylmorpholino-chlorophosphate. Then the arylmorpholino-chlorophosphate reacts with dihydroxy arylene compound with a R₄ group at 70-220° C. in the presence of a catalyst to obtain the oligomeric phosphate ester morpholide compound. In another way, the oligomeric phosphate ester morpholide compound can be prepared by reacting phosphorus oxychloride with dihydroxy arylene compound with a R₄ group, and then reacting the product with aromatic alcohol with a R₃ group. Further, the oligomeric phosphate ester morpholide compound can be prepared by reacting the compounds simultaneously.

The catalyst for preparing the phosphate ester morpholide oligomer includes a metal chloride such as aluminum trichloride (AlCl₃), magnesium chloride (MgCl₂) and zinc chloride (ZnCl₂). Further, a tertiary amine such as triethyl amine can be added to remove hydrogen chloride gas which is formed during the reaction process.

In the process for preparing the phosphate ester morpholide oligomer, if the phosphorus oxychloride (POCl₃) is reacted with an excess of aromatic alcohol with a R₃ group and morpholine, monophosphate ester morpholide with x=y=0 can be obtained, and the amount of the monophosphate ester morpholide with x=y=0 can be controlled by adjusting the process conditions. The oligomeric phosphate ester morpholide compound may be used without or after purification.

(D₂) Phosphoric Acid Ester

The phosphoric acid ester is represented by the following Formula (IV). The phosphoric acid ester may be used in single or in combination as a mixture.

where R₃, R₄, R₅ and R₇ are a C₆₋₂₀ aryl group or an alkyl-substituted C₆₋₂₀ aryl group, respectively, preferably a phenyl group or an alkyl-substituted phenyl group in which alkyl is methyl, ethyl, isopropyl, t-butyl, isobutyl, isoamyl or t-amyl, preferably methyl, ethyl, isopropyl or t-butyl; R₅ is a C₆₋₃₀ arylene group or an alkyl-substituted C₆₋₃₀ arylene group, preferably resorcinol, hydroquinone or bisphenol-A; and l means the number of repeating units and the average value of l in the phosphate mixture is 0 to 3.

In the present invention, it is preferable to use an oligomer type phosphoric acid ester that is a derived from a C₆₋₃₀ arylene group and has an average value of l of about 0 to 3. The oligomer type phosphoric acid ester is a mixture of oligomers in which l is 0, 1, 2 and 3, respectively. The oligomer type phosphoric acid esters are mixed before or after polymerization.

The representative examples of the phosphoric acid ester with l=0 are tri(alkylphenyl)phosphate, di(alkylphenyl)monophenylphosphate, diphenylmono(alkylphenyl)phosphate and triphenylphosphate. The phosphoric acid ester can be used in single or in combination as a mixture. The section relating to the phosphoric acid ester in U.S. Pat. No. 7,094,818 is herein incorporated by reference.

About 1 to 30 parts by weight of a phosphorous mixture of (d₁) about 1 to 50% by weight of a cyclic phosphazene oligomer compound and about 99 to 50% by weight of (d₂) or (D₂) are used per 100 parts by weight of (A)+(B)+(C).

(E) Fluorinated Polyolefin Resin

The examples of the fluorinated polyolefin resin are polytetrafluoroethylene, polyvinylidenefluoride, tetrafluoroethylene/vinylidenefluoride copolymer, tetrafluoroethylene/hexafluoropropylene copolymer, and ethylene/tetrafluoroethylene copolymer. The fluorinated polyolefin resin may be used in single or in combination as a mixture.

The fluorinated polyolefin resin functions to form a fibrillar network when the resin composition containing the fluorinated polyolefin resin is extruded, resulting to increase the flow viscosity and to increase the shrinkage during combustion so as to prevent the dripping phenomena. The fluorinated polyolefin resin may be omitted if the properties provided by the resin are not required or if the properties can be obtained by other materials and/or methods of preparing the compositions containing of (A), (B), and (D) as described previously.

The fluorinated polyolefin resin (E) according to the present invention is prepared by a conventional process, for example, the resin is prepared in an aqueous solvent at 7˜71 kg/cm² and 0˜200° C., preferably 20˜100° C., in the presence of a free radical forming catalyst such as sodium-, potassium-, or ammonium-peroxydisulphate.

The fluorinated polyolefin resin is used in emulsion state or in powder state. In case using in emulsion state, dispersion of the fluorinated polyolefin resin is good, but the process will be somewhat complicated. Accordingly, if the fluorinated polyolefin resin could be uniformly dispersed in the entire resin composition to form the fibrillar network structure, it is preferable to use the fluorinated polyolefin resin in powder state.

The fluorinated polyolefin resin has preferably average particle size of about 0.05 to 1000 μm and density of about 1.2 to 2.3 g/cm³.

The fluorinated polyolefin resin is used in an amount of about 0.05 to 5.0 parts by weight as per 100 parts by weight of (A)+(B)+(C) of the flame retardant thermoplastic resin composition according to the present invention.

Other additives may be contained in the resin composition of the present invention. The additives include an additional flame retardant, a lubricant, a releasing agent, an anti-dripping agent, an impact modifier, a plasticizer, a heat stabilizer, an oxidation inhibitor, a light stabilizer, a compatibilizer and the like. An inorganic filler such as talc, silica, mica, glass fiber, an organic or inorganic pigment and/or dye can be added too. The additives are employed in an amount of about 0 to 60 parts by weight as per 100 parts by weight of (A)+(B)+(C) of the flame retardant thermoplastic resin composition, preferably about 1 to 40 parts by weight.

The flame retardant thermoplastic resin composition according to the present invention can be prepared by a conventional method. All the components and additives are mixed together and extruded through an extruder and are prepared in the form of pellets.

The flame retardant thermoplastic resin composition according to the present invention can be applied to electric or electronic goods, automobile parts, office supplies, etc which require good flame retardancy, weld-line strength and impact strength.

The invention may be better understood by reference to the following examples which are intended for the purpose of illustration and are not to be construed as in any way limiting the scope of the present invention. In the following examples, all parts and percentage are by weight unless otherwise indicated.

EXAMPLES

The components to prepare flameproof thermoplastic resin compositions in Examples 1-6 and Comparative Examples 1-7 are as follows

(A) Polycarbonate Resin

Bisphenol-A with a weight average molecular weight (M_(w)) of about 25,000 was used as polycarbonate resin.

(B) Rubber Modified Vinyl-Grafted Copolymer

(B₁) 50 parts of butadiene rubber latex, 36 parts of styrene, 14 parts of acrylonitrile and 150 parts of deionized water were mixed. To the mixture, 1.0 parts of potassium oleate, 0.4 parts of cumenhydroperoxide, and 0.3 parts of t-dodecyl mercaptane chain transfer agent were added. The blend was kept at 75° C. for 5 hours to obtain ABS latex. To the ABS latex, 1% sulfuric acid was added, coagulated and dried to obtain styrene-containing graft copolymer resin (g-ABS) in powder form.

(B₂) A graft copolymer of EXL-2602 (product name) by Kureha Co. was used, in which methacrylic acid ester monomers are grafted onto butadiene rubber.

(C) Vinyl Copolymer

71 parts of styrene, 29 parts of acrylonitrile, 120 parts of deionized water and 0.2 parts of azobisisobutylonitrile (AIBN) were blended. To the blend, 0.5 parts of tricalciumphosphate and 0.3 parts of mercaptan-containing chain transfer agent were added. The resultant solution was heated to 80° C. for 90 minutes and kept for 180 minutes. The resultant was washed, dehydrated and dried. Styrene-acrylonitrile copolymer (SAN) was obtained.

(D) Phosphorous Compound

(d₁) Cyclic Phosphazene Oligomer

The cyclic phosphazene oligomer is a mixture of: 66.5% by weight of an oligomer of Formula (I) in which R₁ is phenoxy, k and m are 1 or 2, and n is 0; 20.3% by weight of an oligomer of Formula (II) in which R₁ is phenoxy, R₂ is a derivative from resorcinol, k and m are 1 or 2, and n is 1; 4.9% by weight of an oligomer of Formula (II) in which R₁ is phenoxy, R₂ is a derivative from resorcinol, k and m are 1 or 2, and n is 2; and 8.3% by weight of an oligomer of Formula (II) in which R₁ is phenoxy, R₂ is a derivative from resorcinol, k and m are 1 or 2, and n is 3 or more.

(d₂) Phosphate Ester Morpholide

(d_(2a)) This phosphate ester morpholide contains 9% by weight of triphenylphosphate (TPP), and 91% by weight of a monophosphate ester morpholide represented by the chemical Formula (II) where R₃ is a phenyl group, which consists of 88% by weight of the compound of l=1 and x=y=0, and 3% by weight of the compound of l=2 and x=y=0.

(d_(2b)) This phosphate ester morpholide was obtained by reacting resorcinol with phenyl morpholino chlorophosphate and represented by the chemical Formula (II) where R₃ is a phenyl group and R₄ is a resorcinol derivative, containing 1.5% by weight of phosphate ester morpholide where l=1 and x=y=0; 68.4% by weight phosphate ester morpholide where l=1 and x+y=1; and 30.1% by weight phosphate ester morpholide where l=1 and x+y=2 or more.

(d₃) Linear Cross-linked Phosphazene

The phosphazene used in the Comparative Examples is a mixture of linear cross-linked phosphazene oligomers. The mixture was prepared to link 62% by weight of phenoxy phosphazene trimer, 12% by weight of phenoxy phosphazene tetramer, and 26% by weight of phenoxy phosphazene pentamer or more with hydroquinone. The molar ratio of phenoxy to hydroquinone is 1.7 to 0.15 and the weight average molecular weight is about 1100.

(E) Fluorinated Polyolefin Resin

Teflon (registered trademark) 7AJ by Dupont company was used.

Examples 1-6 and Comparative Examples 1-7

The resin compositions of Examples 1-6 and Comparative Examples 1-7 were prepared as in Tables 1 and 2. The mechanical properties are shown in the Tables.

Comparative Example 1 was conducted in the same manner as in Example 1 except that the phosphorous mixture with the composition out of the claimed range was used as in Table 2.

Comparative Examples 2-4 were conducted in the same manner as in Example 1 except that a single phosphorous compound was used as in Table 2.

Comparative Example 5 was conducted in the same manner as in Example 2 except that a linear phosphazene oligomer was used as in Table 2.

Comparative Example 6 was conducted in the same manner as in Example 6 except that a phosphate ester morpholide only was used as in Table 2.

Comparative Example 7 was conducted in the same manner as in Example 6 except that a linear phosphazene oligomer was used as in Table 2.

The components as shown in Tables 1 and 2, an antioxidant and a heat stabilizer were mixed in a conventional mixer and the mixture was extruded through a twin screw extruder with L/D=35 and Ø=45 mm at 240° C. to prepare in pellet form. The resin pellets were molded into test specimens for measuring flame retardancy and mechanical properties using a 10 oz injection molding machine at 240° C. The specimens were kept at the relative humidity of 50% at 23° C. for 48 hours. The physical properties were measured in accordance with ASTM regulations.

The mechanical properties of the test specimens of Examples 1-6 and Comparative Examples 1-7 were measured as follow:

The flexural strength was measured in accordance with ASTM D790.

The flame retardancy was measured in accordance with UL94VB. The test specimens have a thickness of 1.6 mm.

For each Example, five specimens were tested twice. The total flame out time is the sum of the first flame out time and the second flame out time.

The melt flow index was measured in accordance with ASTM D1238 under 220° C./10 kgf.

The heat distortion temperature was measured in accordance with ASTM D648 under 18.6 kgf.

TABLE 1 Examples 1 2 3 4 5 6 (A) 80 80 80 80 80 95 (B) (B₁) 10 10 10 10 10 — (B₂) — — — — — 5 (C) 10 10 10 10 10 — (D) (d₁) 1 3 5 2 2 1 (d_(2a)) 2 2 1 — 10 2 (d_(2b)) 9 7 6 10 — 2 (d₃) — — — — — — (E) 0.5 0.5 0.5 0.5 0.5 0.4 UL94VB ( 1/16″) V-0 V-0 V-0 V-0 V-0 V-0 Total Flame Out Time (sec) 14 17 16 17 11 12 Flexural Strength 845 855 855 850 855 905 HDT 91 92 95 96 90 121 MFI 34 32 30 31 35 19

TABLE 2 Comparative Examples 1 2 3 4 5 6 7 (A) 80 80 80 80 80 95 95 (B) (B₁) 10 10 10 10 10 — — (B₂) — — — — — 5 5 (C) 10 10 10 10 10 — — (D) (d₁) 9 12 — — — — — (d_(2a)) 1 — — 12 1 2 2 (d_(2b)) 2 — 12 — 6 3 2 (d₃) — — — — 5 — 1 (E) 0.5 0.5 0.5 0.5 0.5 0.4 0.4 UL94VB ( 1/16″) V-1 V-1 V-2 V-1 V-1 V-1 V-1 Total Flame Out Time (sec) 58 69 115 57 69 71 66 Flexural Strength 825 815 825 835 835 890 895 HDT 96 101 91 85 94 120 120 MFI 24 19 31 35 30 21 21

As shown in Tables 1 and 2, the resin compositions employing a phosphorous mixture of cyclic phosphazene oligomer and phosphate ester morpholide show synergistic effect in flame retardancy and flexural strength with no big difference in heat distortion temperature and melt flow index, compared to those employing a single phosphorous compound. The resin composition using a linear phosphazene oligomer shows a poor flame retardancy.

The examples of parent U.S. Pat. No. 7,094,818 in their entirety are herein incorporated by reference. 

1-10. (canceled)
 11. A flame retardant thermoplastic resin composition comprising: (A) about 45 to 95 parts by weight of a polycarbonate resin; (B) about 1 to 50 parts by weight of a rubber modified vinyl-grafted copolymer prepared by graft-polymerizing (b₁) about 5 to 95 parts by weight of a monomer mixture consisting of about 50 to 95% by weight of at least one selected from the group consisting of styrene, α-methylstyrene, halogen- or alkyl-substituted styrene, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, and a mixture thereof and about 5 to 50% by weight of acrylonitrile, methacrylonitrile, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, maleic acid anhydride, or C₁₋₄ alkyl- or phenyl N-substituted maleimide onto (b₂) about 5 to 95 parts by weight of a rubber polymer selected from the group consisting of butadiene rubber, acryl rubber, ethylene-propylene rubber, styrene-butadiene rubber, acrylonitrile-butadiene rubber, isoprene rubber, copolymer of ethylene-propylene-diene (EPDM), polyorganosiloxane-polyalkyl (meth)acrylate rubber and a mixture thereof; (C) about 0 to 50 parts by weight of a vinyl copolymer polymerized with (c₁) about 50 to 95% by weight of at least one of styrene, α-methylstyrene, halogen- or alkyl-substituted styrene, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester or a mixture thereof and (c₂) about 5 to 50% by weight of at least one of acrylonitrile, methacrylonitrile, C₁₋₈ methacrylic acid alkyl ester, C₁₋₈ acrylic acid alkyl ester, maleic acid anhydride, C₁₋₄ alkyl- or phenyl N-substituted maleimide or a mixture thereof; (D) about 1 to 30 parts by weight of a mixture, as a flame retardant, per 100 parts by weight of (A)+(B)+(C), of (d₁) about 1 to 50% by weight of a cyclic phosphazene oligomer compound or mixture thereof represented by the following formula;

where R₁ is alkyl, aryl, alkyl substituted aryl, aralkyl, alkoxy, aryloxy, amino or hydroxyl, k and m are an integer from 1 to 10, R₂ is dioxyarylene group of C₆₋₃₀ or a derivative thereof, and n is 0 or an integer representing the number of repeating unit and the average value of n in the phosphazene mixture is 0.3 to 3; and about 99 to 50% by weight of (d₂) or (D₂) wherein (d₂) is a phosphate ester morpholide represented by the following formula;

where R₃ is a C₆₋₂₀ aryl group or an alkyl-substituted C₆₋₂₀ aryl group, R₄ is a C₆₋₃₀ arylene group or an alkyl-substituted C₆₋₃₀ arylene group, l is 1 or 2, and x and y are 0 or integers representing the number of corresponding units and the average value of (x+y) in the mixture of phosphate ester morpholide compounds is 0 to 5; (D₂) is a phosphoric acid ester represented by the following Formula (IV);

where R₃, R₄, R₅ and R₇ are a C₆₋₂₀ aryl group or an alkyl-substituted C₆₋₂₀ aryl group, respectively; R₅ is a C₆₋₃₀ arylene group or an alkyl-substituted C₆₋₃₀ arylene group; and l means the number of repeating unit and the average value of l in the phosphate mixture is 0 to 3; and, (E) about 0.05 to 5.0 parts by weight of a fluorinated polyolefin resin with average particle size of about 0.05 to 1000 μm and density of about 1.2 to 2.3 g/cm³, per 100 parts by weight of (A)+(B)+(C).
 12. The flame retardant thermoplastic resin composition as defined in claim 11, wherein said cyclic phosphazene oligomer compound has a linear structure or a structure with a branched chain at the main chain.
 13. The flame retardant thermoplastic resin composition as defined in claim 11, wherein R₁ is phenoxy and R₂ is a derivative from catechol, resorcinol, hydroquinone, or the bisphenylenediol represented by the following formula:

where Y is alkylene of C₁₋₅, alkylidene of C₁₋₅, cycloalkylidene of C₅₋₆, S or SO₂, and z is 0 or
 1. 14. The flame retardant thermoplastic resin composition as defined in claim 11, wherein said R₃, R₄, R₆ and R₇ in Formula (IV) are a phenyl group or an alkyl-substituted phenyl group where the alkyl is methyl, ethyl, isopropyl or t-butyl, and R₅ is a derivative from resorcinol, hydroquinone, or bisphenol-A.
 15. A molded article produced from the flame retardant thermoplastic resin composition as defined in claim
 11. 16-25. (canceled) 